LATP Li1.3Al0.3Ti1.7P3O12 Solid State Battery Electrolyte Sheet
Technical Parameters
LATP solid state battery electrolyte has received extensive attention because of its excellent chemical and thermodynamic stability, extremely low raw material cost and preparation cost. It is a nano-solid electrolyte material that can be used for the preparation of all-solid-state lithium-ion batteries.
Model: XW-LATP-E01
Conductivity: 2*10-4S/cm
Optional specifications:
1. Square 60*60mm
2. Single piece packaging with diameter of 12mm*260μm
3. Other sizes can be customized
| Product name | Lithium Aluminum Titanium Phosphate Solid State Battery Electrolyte Sheet | ||
| Specification | Round sheet, diameter 12mm, thickness 260μm | ||
| Theoretical density | 2.94g/cm3 | ||
| Chemical formula | Li1.3Al0.3Ti1.7P3O12 | ||
| Shelf life | 1 year | ||
| Items | Qualification standards | Unit | Detection method |
| Thickness | 260±10 | μm | Micrometer |
| Diameter | 12±0.1 | mm | Vernier caliper |
| Appearance | White, uniform color | / | Visual inspection |
| Main crystal phase | Consistent with the characteristic peak of PDF#35-0754 | / | XRD |
| Ceramic sample ion conductivity@25℃ | ≥0.45 | mS/cm | AC impedance method |
| Flexural strength | ≥130 | MPa | Three-point bending resistance |
| Density | ≥2.793 | g/cm3 | Drainage method |
| Densification | ≥95 | % | Density/theoretical density*100% |
| Micromorphology | Magnification 20000, no more than 3 holes | / | SEM |