LiCoO2 (High-Voltage) S-4.48V

Item No.: XW-CA-0007;
Application: LiCoO2 (high voltage type) – S-4.48V;
Warranty: One Year warranty with lifetime support;
Payment: T/T,Western Union, Paypal,L/C;
Product Origin: China;
Lead Time: in stock or 1-10days,ect;
Note: XIAOWEI factory supports OEM.

 Products Description 

Electrochemical performance test data is for reference only and may vary due to different testing methods.

  1. Due to the larger particle size and high compacted density of high voltage LiCoO2, the pressure needs to be increased during the rolling process.
  2. When using high voltage LiCoO2 for high voltage applications, attention should be paid to the matching use of electrolyte to prevent unstable high voltage.

Physical Property: First efficiency and capacity test conditions: temperature25℃, first constant current charge to 4.45V, then constant voltage charge until the current is less than 0.02C, and then constant current discharge at 0.1C to3.0V.

 Technical Parameters 

D10 (um) ≥3.5
D50 (um) 16.0±2.0
D90 (um) ≤45.00
Gram capacity (mAh/g) 178
Gram capacity power-off test conditions RT test at room temperature, 3.0~4.45V, 0.1C/0.1C
Specific surface area (m2/g) 0.16±0.06
Vibration density (g/cm3) ≥2.50


  • LiCoO2, single crystal structure, with high specific capacity, surface modification coating, suitable for high voltage (>4.45V), large and small particle mix, high compacted density, and good cycling performance.
  • Good processing performance, commercial mass production products with stable quality.
  • Widely used in high energy density products such as smartphones, smart wristbands, and tablets.
  • Convenient for research on soft pack and button battery.