Lithium cobalt oxide (magnification type) – C

Battery Process

More Custom Items

Lithium cobalt oxide (magnification type) – C

Item No.: XW-EN-CA-0004;
Application: Lithium cobalt oxide (magnification type)-C;
Order(MOQ): 1 set;
Payment: T/T,Western Union, Paypal,L/C;
Product Origin: China;
Lead Time: in stock or 1-10days,ect;
Note: XIAOWEI factory supports OEM.

 Products Description 

1. Due to the small particle size and large specific surface area of the material, compared with the positive electrode formula of ordinary LiCoO2, more conductive and adhesive agents are required to ensure good electronic transmission network.

2. Due to the small particle size, the compaction density of the electrode sheet is 0.3-0.5g/cc lower than that of conventional LiCoO2.

Advantage:

  1. lithium cobalt oxide, single crystal structure, with small particle size and large specific surface area, facilitating rapid insertion and extraction of lithium ions, resulting in excellent rate performance and good cycling stability.
  2. Good processability and stable quality for commercial mass production.
  3. Widely used in high-rate requirement products such as drones and electronic cigarettes.
  4. Convenient for research on flexible packaging and button cells.

 Technical Parameters 

D10 (um) 4.061
D50 (um) 6.956
D90 (um) 11.687
Gram capacity (mAh/g) 142
Gram capacity power-off test conditions 25℃ 0.1C 3.0~4.2V
Specific surface area (m2/g) 0.39
Vibration density (g/cm3) 2.29

Physical Property:

  • Initial efficiency and capacity testing conditions: Temperature 25℃. Charge at a constant current (0.1C) to 4.3V, then charge at a constant voltage until the current is less than 0.02C, and discharge at a constant current (0.1C) to 3.0V.
  • Rate testing conditions: Temperature 25℃. Charge at a constant current (0.5C) to 4.3V, then charge at a constant voltage until the current is less than 0.02C. Then, discharge at constant currents (0.1C/0.2C/0.5C/1C/2C/3C) to 3.0V.
  • Cycle testing conditions: Temperature 25℃. Charge at a constant current (0.5C) to 4.3V, then charge at a constant voltage until the current is less than 0.02C. Discharge at a constant current (1C) to 3.0V.

Storage:

  • Storage conditions: Store at room temperature in a sealed manner.
  • Shelf life: 2 years from the production date.