Lithium Manganese Oxide-X (LiMnO-X)

Battery Process

More Custom Items

Lithium Manganese Oxide-X (LiMnO-X)

Item No.: XW-EN-CA-0016;
Application: Lithium Manganese Oxide-X (LiMnO-X);
Warranty: One Year warranty with lifetime support;
Payment: T/T,Western Union, Paypal,L/C;
Product Origin: China;
Lead Time: in stock or 1-10days,ect;
Note: XIAOWEI factory supports OEM.

 Products Description 

Electrochemical performance test data is for reference only and may vary due to different testing methods.

1. The material has high maturity and good processing properties.

2. It can be used alone or in combination to reduce costs.

3. This material has poor performance at high temperatures due to the dissolution of manganese.

4. Compression is recommended to be controlled at around 3.0g/cm3 (2.9-3.1g/cm3).

Advantage:

  1. Lithium manganese oxide with spinel structure has high specific capacity, high volumetric density, good cycle performance, structural stability, good safety, and low-temperature performance.
  2. It has excellent processing performance, commercialized mass production products, good quality, and stable performance.
  3. Widely used in power tools, low-speed electric vehicles, and other products.
  4. Convenient for research on pouch cells and coin cells.
  5. Due to the extensive use of low-cost manganese to replace the scarce and expensive resources of cobalt and nickel in this material, the cost of the material is the lowest.

 Technical Parameters 

D10 (um) ≥3.50
D50 (um) 13.00~17.00
D90 (um) ≤40.00
Gram capacity (mAh/g) 117
Gram capacity power-off test conditions RT test at room temperature, 3.0~4.3V, 0.1C/0.1C
Specific surface area (m2/g) 0.40~0.80
Vibration density (g/cm3) ≥2.00

Physical Property:

  • Initial efficiency and capacity testing conditions: Temperature 25℃. Charge at a constant current (0.1C) to 4.3V, then charge at a constant voltage until the current is less than 0.02C, and discharge at a constant current (0.1C) to 3.0V.
  • Rate testing conditions: Temperature 25℃. Charge at a constant current (0.5C) to 4.3V, then charge at a constant voltage until the current is less than 0.02C. Then, discharge at constant currents (0.1C/0.2C/0.5C/1C/2C/3C) to 3.0V.
  • Cycle testing conditions: Temperature 25℃. Charge at a constant current (0.5C) to 4.3V, then charge at a constant voltage until the current is less than 0.02C. Discharge at a constant current (1C) to 3.0V.

Storage:

  • Storage conditions: Store at room temperature in a sealed manner.
  • Shelf life: 2 years from the production date.